5a05 is a type of aluminum alloy that belongs to the Al Mg series. Unlike other alloys in this series, it cannot be strengthened through heat treatment. It contains a higher amount of magnesium and has lower strength, similar to the 5A03 alloy. When these alloys undergo cold deformation, their strength increases but their plasticity decreases. In its annealed state, 5a05 has relatively high plasticity, while in the semi cold worked hardened state, it still maintains an acceptable level of plasticity. This alloy is known for its good corrosion resistance and weldability. It can be used for spot welding, atomic hydrogen welding, gas welding, and argon arc welding. However, its machinability and annealing state are poor, while the semi cold work hardening state is still acceptable.
5a05 is a type of aluminum alloy that belongs to the Al Mg series. Unlike other alloys in this series, it cannot be strengthened through heat treatment. It contains a higher amount of magnesium and has lower strength, similar to the 5A03 alloy. When these alloys undergo cold deformation, their strength increases but their plasticity decreases. In its annealed state, 5a05 has relatively high plasticity, while in the semi cold worked hardened state, it still maintains an acceptable level of plasticity. This alloy is known for its good corrosion resistance and weldability. It can be used for spot welding, atomic hydrogen welding, gas welding, and argon arc welding. However, its machinability and annealing state are poor, while the semi cold work hardening state is still acceptable.
Product | Contract No. | Lot No. | ||||||||||
Dimension (mm) | 1.2-200 | Alloy | 5A05 | Piece Count | ||||||||
Techuique Standard | GB/T3190--1996/EN | Weight(kg) | ||||||||||
Chemical Composition(%) | ||||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Others | Al | ||
Standard | 0.5 | 0.5~1.0 | 0.1 | 0.3-0.6 | 4.8-5.5 | - | - | 0.2 | 0.15 | 0.15 | Remain | |
Notice:Aluminum foil not contains Pb、As and other Virose elements | ||||||||||||
Mechanical Property | ||||||||||||
Temper | Thickness | Tensile Strength(Mpa) | Strength(Mpa) | Elongation% | Cup Bulge | |||||||
O | 1.2-6.3 | 290-365 | 130-205 | - | - | |||||||
6.31-80 | 285-360 | 125-205 | 14 | - | ||||||||
80.1-120 | 275 | 120 | 12 | - | ||||||||
120.1-160 | 270 | 115 | 12 | - | ||||||||
160.1-200 | 265 | 105 | 10 | - | ||||||||
H112 | 6.3-40 | 290 | 130 | 10 | - | |||||||
40.1-80.0 | 285 | 125 | 10 | - | ||||||||
H116 | 1.6-30 | 315 | 230 | 10 | - | |||||||
30.1-40 | 305 | 215 | 10 | - | ||||||||
40.1-80.0 | 285 | 200 | 10 | - | ||||||||
80.1-110 | 275 | 170 | 10 | - | ||||||||
H321 | 4.0-12.5 | 315-405 | 230-315 | - | - | |||||||
12.51-40.0 | 305-385 | 215-305 | 10 | - | ||||||||
40.1-80.0 | 385-385 | 200-295 | 10 | - | ||||||||
H323 | 1.2-6.3 | 330-400 | 250-315 | - | - | |||||||
H343 | 1.2-6.3 | 365-435 | 285-350 | - | - | |||||||
Product | Contract No. | Lot No. | ||||||||||
Dimension (mm) | 1.2-200 | Alloy | 5A05 | Piece Count | ||||||||
Techuique Standard | GB/T3190--1996/EN | Weight(kg) | ||||||||||
Chemical Composition(%) | ||||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Others | Al | ||
Standard | 0.5 | 0.5~1.0 | 0.1 | 0.3-0.6 | 4.8-5.5 | - | - | 0.2 | 0.15 | 0.15 | Remain | |
Notice:Aluminum foil not contains Pb、As and other Virose elements | ||||||||||||
Mechanical Property | ||||||||||||
Temper | Thickness | Tensile Strength(Mpa) | Strength(Mpa) | Elongation% | Cup Bulge | |||||||
O | 1.2-6.3 | 290-365 | 130-205 | - | - | |||||||
6.31-80 | 285-360 | 125-205 | 14 | - | ||||||||
80.1-120 | 275 | 120 | 12 | - | ||||||||
120.1-160 | 270 | 115 | 12 | - | ||||||||
160.1-200 | 265 | 105 | 10 | - | ||||||||
H112 | 6.3-40 | 290 | 130 | 10 | - | |||||||
40.1-80.0 | 285 | 125 | 10 | - | ||||||||
H116 | 1.6-30 | 315 | 230 | 10 | - | |||||||
30.1-40 | 305 | 215 | 10 | - | ||||||||
40.1-80.0 | 285 | 200 | 10 | - | ||||||||
80.1-110 | 275 | 170 | 10 | - | ||||||||
H321 | 4.0-12.5 | 315-405 | 230-315 | - | - | |||||||
12.51-40.0 | 305-385 | 215-305 | 10 | - | ||||||||
40.1-80.0 | 385-385 | 200-295 | 10 | - | ||||||||
H323 | 1.2-6.3 | 330-400 | 250-315 | - | - | |||||||
H343 | 1.2-6.3 | 365-435 | 285-350 | - | - | |||||||
Productivity: 1200 tons per month Transportation: Ocean,Land
Place of Origin: China Supply Ability: 1050 tons per month
Certificate: ISO9001 HS Code: 76061199
Payment Type: L/C,T/T In co term: FOB,CFR,CIF,EXW
Productivity: 1200 tons per month Transportation: Ocean,Land
Place of Origin: China Supply Ability: 1050 tons per month
Certificate: ISO9001 HS Code: 76061199
Payment Type: L/C,T/T In co term: FOB,CFR,CIF,EXW
Commonly used in manufacturing welded pipelines, welded oil tanks, and other liquid containers that require high process shaping, good corrosion resistance, and medium load capacity, as well as other parts; Wire used as welding rods and rivets requires anodizing treatment. It is also used for making armor plates, high-strength structural components, storage tanks, pressure vessels, and marine product components
Commonly used in manufacturing welded pipelines, welded oil tanks, and other liquid containers that require high process shaping, good corrosion resistance, and medium load capacity, as well as other parts; Wire used as welding rods and rivets requires anodizing treatment. It is also used for making armor plates, high-strength structural components, storage tanks, pressure vessels, and marine product components